    Atlas F

    Atlas F has a very good honeycomb structure and special chemical properties, which can be effectively used in all standard industries and processing industries, such as hand lay-up, vacuum infusion, RTM and other processes. It is a globally applicable material, widely used in fields such as wind turbine cabin covers, ships and non-structural parts.

    1. Detailed information

    产品特点 / Features

    ■ Excellent fatigue resistance                                                        

    ■ Suitable for dynamic load structure                                 

    ■ Higher resistance to styrene                    

    ■ Higher temperature resistance                                                                               

    ■ Resin injection is more ideal                                              

    ■ Less resin consumption than other foams               

    ■ Recyclable                                                                                                                                      

    典型心梗 Typical Performance单位 UnitF50 F60F65F80F100

    密度区间

    Density Range

    ASTM-D1622Kg/m³45-5557-6562-7272-8888-108
    压缩强度

    Compressive Strength

    ASTM-D1621MPa0.400.551.23.87.0

    压缩模量

    Compressive Modulus

    ASTM-D1621MPa2030354570

    拉伸强度

    Tensile Strength

    ASTM-D1623MPa0.400.550.800.801.10

    拉伸模量

    Tensile Modulus

    ASTM-D1623MPa2235405070

    剪切强度

    Shear Strength

    ASTM C273MPa0.350.480.600.600.75

    剪切模量

    Shear Modulus

    ASTM C273MPa5.07.510.012.015.0
    剪切伸长率

    Shear Elongation

    ASTM C273%2525252015
    吸水率

    Water Absorption

    ISO 2896%2221.51.5

    初始热导率

    Initial Thermal Conductivity

    ASTM C518mW/mK2424242525

    热变形温度

    Heat Distortion Temperature

    DIN- 53424100110110120120

    使用温度

    Service Temperature

    /-180,+95-180,+195-180,+195-180,+105-180,+105

    阻燃性

    Fire Behaviour

    DIN 4102-1ClassB3B3B3B3B3